龙泉青瓷冰裂纹形成的影响因素  

The Influencing Factors of Ice Crack Formation in Longquan Celadon

作　　者：刘干平 吴义祥 刘艳飞[2] Liu Ganping;Wu Yixiang;Liu Yanfei(Dingqingqing Porcelain Workshop,Longquan,323700;Yiwu Vocational and Technical College of Industry and Commerce,Yiwu,322000)

机构地区：[1]龙泉市鼎青青瓷坊,龙泉323700 [2]义乌工商职业技术学院,义乌322000

出　　处：《陶瓷研究》2024年第6期82-85,88,共5页Ceramic Studies

基　　金：2022年度浙江省软科学研究计划项目(项目编号:2022C35001)。

摘　　要：本文以龙泉青瓷为基础,分别用钾长石、钠长石、霞石代替其中的黄坛瓷土,配制4种釉,施于龙泉弟窑白胎和哥窑黑胎上,进行一系列的烧制试验,根据烧成结果,观察烧成制品裂纹的变化特征以及冰裂纹的形成状况,从釉料的化学组成、烧成温度、釉层厚度和胎体组成四个方面阐述冰裂纹形成的影响因素和影响规律。This article is based on Longquan celadon and uses potassium feldspar,sodium feldspar,and nepheline to replace the Huangtan porcelain clay.Four types of glazes are prepared and applied to the white and black bodies of Longquan Di kiln and Ge kiln.A series of firing experiments are conducted.Based on the firing results,the characteristics of cracks in the fired products and the formation of ice cracks are observed.The influencing factors and laws of ice crack formation are explained from four aspects:chemical composition of the glaze,firing temperature,glaze layer thickness,and matrix composition.continue to develop well.

关 键 词：龙泉青瓷 冰裂纹 釉料和胎体 烧成温度 釉层厚度 

分 类 号：TQ174.43[化学工程—陶瓷工业]