Effect of interlayer cold joint on mechanical properties and permeability of roller compacted concrete  

作　　者：Sultan Husein BAYQRA SüleymanÖZEN Ali MARDANI Kambiz RAMYAR 

机构地区：[1]Department of Civil Engineering,Faculty of Engineering,Bursa Uludag University,Nilüfer 16059,Turkey [2]Department of Civil Engineering,Faculty of Engineering and Natural Sciences,Bursa Technical University,Yildirim 16330,Turkey [3]Department of Civil Engineering,Faculty of Engineering,Ege University,Bornova 35100,Turkey

出　　处：《Frontiers of Structural and Civil Engineering》2025年第2期284-299,共16页结构与土木工程前沿(英文版)

基　　金：gratefully acknowledge the support of the Scientific and Technological Research Council of Turkey(TUBITAK)(No.217M408);the Bursa UludağUniversity Science and Technology Centre(BAP)(No.AYP(MH)-2016/16)。

摘　　要：One issue with layer application of roller compacted concrete(RCC)is the development of cold joints,which can cause damage to RCC structures.In this study,fly ash was used in place of 0%,20%,40%,and 60%of the cement or aggregate to examine the impact of interlayer cold joint formation on RCC mixtures.To promote cold joint formation,the second layer was placed and compacted with a delay of 0,60,120,or 180 min after the first layer.Three methods were tried for preventing cold joints from forming:one was to apply a bedding mortar to the interlayer,another was to add a set retarder admixture,and the third was to spray an adhesion-enhancing chemical additive on the surface of the first layer.Based on the 28 d specimens’compressive and splitting-tensile strengths as well as the depth of water penetration under pressure,the most effective method was found to be applying interlayer bedding mortar.Considering 180 min delayed layer castings,the splitting-tensile and compressive strengths of the control samples decreased by 31%and 17%,respectively,while the strengths of mixtures applying interlayer bedding mortar decreased by 9%and 10%.In addition,bedding mortar treatment decreased the water permeability by 59%compared to the control.Interlayer cold joint decreased all mixtures’moduli of elasticity,regardless of the age of the specimens.When the interlayer delay was 60 min,the modulus of elasticity decreased by 1%–4%.It was between 2%and 14%,and between 10%and 24%at 120 and 180 min for the interlayer delay.The longer the delay in placing the second RCC layer,the more detrimental the effect of the cold joint.This effect was most noticeable on mechanical and permeability properties tested with applied load or water pressure parallel to the cold joint,such as flexural and splitting tensile strengths and water penetration depth under pressure.

关 键 词：roller compacted concrete cold joint mechanical properties permeability properties fly ash 