硅铝矿物组分对垃圾焚烧飞灰熔融特性与重金属固化的影响  

Effects of silicon-aluminum mineral components on the melting characteristics and the solidification of heavy metal of municipal solid waste incineration fly ash

作　　者：高嘉炜 黄亚继[1] 王圣 朱志成 肖怡萱 宋惠康 刘俊[1] 祁帅杰 张煜尧 赵佳琪 GAO Jiawei;HUANG Yaji;WANG Sheng;ZHU Zhicheng;XIAO Yixuan;SONG Huikang;LIU Jun;QI Shuaijie;ZHANG Yuyao;ZHAO Jiaqi(Key Laboratory of Energy Thermal Conversion and Control of Ministry of Education,Southeast University,Nanjing 210096,Jiangsu,China;State Key Laboratory of Clean and Efficient Coal-fired Power Generation and Pollution Control,Nanjing 210023,Jiangsu,China)

机构地区：[1]东南大学能源热转换及其过程测控教育部重点实验室,江苏南京210096 [2]清洁高效燃煤发电与污染控制国家重点实验室,江苏南京210023

出　　处：《化工进展》2025年第3期1716-1725,共10页Chemical Industry and Engineering Progress

基　　金：江苏省科技计划(BE2022604,BE2021701)。

摘　　要：熔融法是无害化处置垃圾焚烧(MSWI)飞灰的有效方法。本文开展了硅铝添加剂与飞灰的共熔实验研究,分析了不同硅铝矿物组分对飞灰熔融特性及重金属固化效果的影响。研究发现,硅铝组分和热处理温度对飞灰熔融和重金属的氯化挥发影响较大,其中,SiO_(2)的加入可有效降低飞灰的熔融温度,且添加量为20%时,产物中开始大量出现无定形玻璃体,适量Al_(2)O_(3)的加入有助于重金属的固化,但对飞灰的熔融无明显促进作用;高温和硅铝组分的加入有利于促进重金属的直接或间接氯化反应,使其以氯化物形式挥发,同时生成碱金属硅铝酸盐;此外,蒙脱土在促进飞灰熔融以及固化重金属等方面均优于高岭土,且热处理产物的多次浸出毒性均满足国标限值。Melting is an efficient method for harmless disposal of municipal solid waste incineration fly ash.Experimental study on the co-melting of silica-aluminum additives with fly ash was carried out to analyze the effects of different silica-aluminum mineral components on the melting characteristics and the solidification of heavy metals of fly ash.It was found that the silica-aluminum components and thermal treatment temperature had significant impacts on the melting of fly ash and the chlorinated volatilization of heavy metals.Among them,the addition of SiO_(2)could effectively reduce the melting temperature of fly ash.When the addition amount was 20%,a large number of amorphous vitreous bodies began to appear in the product.The addition of a moderate amount of Al_(2)O_(3)helped the solidification of heavy metals,but it had no obvious promotion effect on the melting of fly ash.High temperature and the addition of Si-Al mineral components were conducive to the promotion of the direct or indirect chlorination of heavy metals,making them volatilize in the form of chlorides,while alkali metal silica-aluminates were produced.In addition,montmorillonite was superior to kaolin in promoting the melting of fly ash and solidifying heavy metals,and the continuous leaching toxicity of the thermal treatment products could meet the standards.

关 键 词：垃圾焚烧飞灰 硅铝矿物组分 熔融 重金属 氯化反应 连续浸出 

分 类 号：X705[环境科学与工程—环境工程]