茂金属聚乙烯催化剂比表面积实验条件的研究  

Study on the Determination Method of the Specific Surface Area of Metallocene Polyethylene Catalyst

作　　者：邴淑秋 沈刚 荣丽丽 靳丽丽 王立娟 Bing Shuqiu;Shen Gang;Rong Lili;Jin Lili;Wang Lijuan(PetroChina Petrochemical Research Institute Daqing Chemical Engineering Research Center,Daqing 163714,China)

机构地区：[1]中国石油石油化工研究院大庆化工研究中心,黑龙江大庆163714

出　　处：《炼油与化工》2025年第2期26-30,共5页Refining And Chemical Industry

摘　　要：采用手套箱取样,氮气吸附法测定茂金属聚乙烯催化剂比表面积、孔体积和孔径。考察了不同取样方式下的物理吸附—脱附曲线及不同脱气温度和脱气时间对比表面积、孔体积和平均孔径测定结果的影响,验证了方法的精密度。实验结果表明,手套箱取样避免了茂金属聚乙烯催化剂接触空气,防止发生氧化和失活;选择低温70℃、脱气4 h条件下脱气,确保了结果的准确性,测定结果的相对标准偏差(RSD)均小于2%,满足分析测试要求。The specific surface area,pore volume and pore size of metallocene polyethylene catalyst were determined by glove box sampling and low temperature nitrogen adsorption method.The effects of physical adsorption-desorption curves,degassing temperature and degassing time on the measured results of surface area,pore volume and pore diameter were investigated,and the precision of the method was verified.The experimental results show that the glove box sampling can prevent the metallocene polyethylene catalyst from contacting the air and prevent oxidation and deactivation.Degassing at a low temperature of 70℃for 4 h was selected to ensure the accuracy of the results,and the relative standard deviation(RSD)of the measured results was less than 2%,which met the requirements of analysis and test.

关 键 词：茂金属聚乙烯催化剂 氮气吸附法 比表面积 孔体积 平均孔径 

分 类 号：TQ426.94[化学工程]