变形六方ZnS纳米晶的固相合成及其荧光特性  

Preparation of Pseudo-hexagonal ZnS Nano-crystal line by Solid-phase Method and its Fluorescent Characteristics

作　　者：丁云峰[1] 余锡宾[1] 贺香红[1] 熊娟[1] 王则民[1] 

机构地区：[1]上海师范大学生命与环境科学学院,上海200234

出　　处：《上海师范大学学报（自然科学版）》2002年第4期47-51,共5页Journal of Shanghai Normal University(Natural Sciences)

基　　金：上海市科委纳米专项基金资助(BL200127)

摘　　要：以硫化钠与醋酸锌为原料,采用改进的室温(湿)固相合成法制备硫化锌纳米晶。用TEM,XRD,UV,PL等方法研究了硫化锌纳米晶粒径、结构与荧光特性。结果表明,硫化锌纳米晶平均粒径约4.0nm,为六方结构。所制备的样品在400～450nm波段出现强荧光发射,并有光谱分裂现象。光谱分裂的原因可能是乙醇对纳米微粒的表面修饰作用、微量杂质的影响以及小尺寸效应的结果。ZnS is a important functional material. This paper reported the preparation of pseudo-hexagonal ZnS nano-crystal powders used the hydrates of Zn(OAc)2 and Na2S by modified solid-state method at room temperature. The structure of particles was characterized by TEM, XRD, UV, IR, PL methods. Results show that it belongs to the hexagonal system. The mean value of the radius of particles is about 4 nm proved by the TEM image, XRD and UV absorption spectrum. The strong PL emission spectrum and spectrum split have been observed at 400-450nm in the sample. The change of the characteristics of the particles was mainly attributed to the modifying surface and small size effect of nano-particles.

关 键 词：固相合成 荧光特性 硫化锌纳米晶 表面修饰 小尺寸效应 纳米材料 变形六方结构 

分 类 号：TB383[一般工业技术—材料科学与工程]