A Transparent Thin Film with Hexagonal Mesostructure Containing Rhodamine 6G  

作　　者：YunFengYAO MaiShengZHANG 等 

机构地区：[1]SchoolofChemistryandChemicalEngineering,ZhongshanUniversity,Guangzhou510275 [2]LaboratoryofRareEarthChemistryandPhysics,ChangchunInstituteofAppliedChemistry,ChineseAcademyofScience,C

出　　处：《Chinese Chemical Letters》2002年第5期464-467,共4页中国化学快报（英文版）

基　　金：This work was financially supported by a grant from the Science Foundation of Guangzhou (2000-Z-076-01) and Laboratory of Rare Earth Chemistry and Physics; Changchun Institute of Applied Chemistry; Chinese Academy of Science.

摘　　要：A transparent thin film was prepared by depositing the sol-gel mixture for the synthesis of MCM-41 mesoporous molecular sieve doped with rhodamine 6G (R6G) dye on glass substrates. The film of silica-surfactant-R6G materials, which was identified to possess hexagonally ordered mesostructure, was composed of nanocrystallites about 35 nm in diameter and 1-10 mm in thickness. Cleanness of the substrates, concentration of the sol-gel mixture and rate of evaporation of the solvent were the key factors affecting transparency and homogeneity of the film. Moreover, optical change and lack in dye aggregation were observed to the R6G-functionalized MCM-41 thin film in contrast with that in ethanol solution.

关 键 词：transparent thin film MCM-41 mesoporous materials rhodamine 6G. 

分 类 号：TQ615.3[化学工程—精细化工]