A Solid Ag Film Deposited from Solution on Self-assembled Mercaptopropyltrimethoxysilane (MPTS) Monolayer  

作　　者：NongYueHE ZhengChunLIU 等 

机构地区：[1]KeyLabofNewMaterialsandTechnologyofChinaNationalPackagingCorporation,ZhuzhouEngineeringCollege,Zhuzhou412008 [2]KeyLaboratoryforMolecularandBio－molecularElectronicsofMinistryofEd

出　　处：《Chinese Chemical Letters》2002年第8期795-798,共4页中国化学快报（英文版）

基　　金：This research is supported by the Chinese 863 High-Tech Project; Natural Science Foundation of China; the Excellent Teacher抯 Foundation of Ministry of Education; China; High-Tech Project of Jiangsu; Natural Science Foundation of Hunan; China; Edu

摘　　要：Mercaptopropyltrimethoxysilane (MPTS) bearing mercapto groups was used to form self-assembly monolayers (SAMs) on glass substrates by solution extraction. SEM, XRD and rubbing test analysis illustrated that the Ag film on the SAMs-modified glass was more durable than that on the commonly-modified glass and that the crystallinity of Ag film on the SAMs-modified glass was identical with those of the Ag film on the commonly-modified glass and pure Ag.Mercaptopropyltrimethoxysilane (MPTS) bearing mercapto groups was used to form self-assembly monolayers (SAMs) on glass substrates by solution extraction. SEM, XRD and rubbing test analysis illustrated that the Ag film on the SAMs-modified glass was more durable than that on the commonly-modified glass and that the crystallinity of Ag film on the SAMs-modified glass was identical with those of the Ag film on the commonly-modified glass and pure Ag.

关 键 词：SAMS electroless plating Ag MORPHOLOGY structure. 

分 类 号：O614.122[理学—无机化学] O62[理学—化学]