Na_2O-SiO_2-Al_2O_3-NaCl-H_2O体系中ANA和SOD沸石膜的水热合成  

Hydrothermal Synthesis of ANA and SOD Zeolite Membrane in Na_2O-SiO_2-Al_2O_3-NaCl-H_2O System

作　　者：钟鹰[1] 周立志[2] 龙英才[1] 

机构地区：[1]复旦大学化学系分子催化与创新材料实验室 [2]复旦大学高分子科学系聚合物分子工程教育部重点实验室,上海200433

出　　处：《化学学报》2003年第1期63-68,共6页Acta Chimica Sinica

摘　　要：Na2 O SiO2 Al2 O3 NaCl H2 O体系中,以水玻璃和准一水软铝石为原料,分别在堇青石和玻璃载体上水热合成方沸石(ANA)与方钠石(SOD)沸石膜.研究水含量、反应温度、反应时间与多次合成对膜结晶的影响.用XRD,SEM,EDX表征膜的晶相、形貌和化学组成.堇青石负载方沸石膜在对 95 %(wt.)乙醇水溶液的渗透蒸发实验中,水优先透过沸石膜的选择性显示了晶间孔的醇/水分离作用.非计量的NaCl进入到在玻璃载体上成膜的方钠石笼中。The membranes of zeolite ANA (analcime) and zeolite SOD (sodalite) were synthesized in the reactant system of Na2O-SiO2-Al2O3-NaCl-H2O using water glass and boehmite as the raw materials on the support of cordierite and glass, respectively. A study has been made of the influence of the molar ratio of H2O/SiO2 in the reactant, the reaction period, and the multiple synthesis on the crystallization of the membrane. The crystalline phase and the morphology of the membrane synthesized were characterized with XRD, SEM and EDX. The pervaporation of 95% (wt.) ethanol/5% (wt.) water through analcime membrane supported on cordierite showed the separation selectivity preference to water molecules, indicating that the separation process occurs in the pores of ANA zeolite inter-crystallites. Non-stoichiometric NaCl was found in SOD membrane supported on glass, and the photochromic effect exhibited after irradiation with X-ray radiation.

关 键 词：Na2O-SiO2-Al2O3-NaCl-H2O体系 ANA SOD 沸石膜 方沸石 方钠石 水热合成 渗透发 光致变色 分子筛膜 

分 类 号：TQ426[化学工程]