高粘度磁性液体的制备研究  

Investigation on Preparation of Magnetic Liquid with High Viscosity

作　　者：孙维民[1] 金寿日[1] 李志杰[1] 董星龙[1] 董玉伟[1] 

机构地区：[1]沈阳工业大学超微粒子研究室,沈阳110023

出　　处：《润滑与密封》2003年第1期20-21,24,共3页Lubrication Engineering

基　　金：沈阳市科委攻关计划资助项目项目编号 :2 0 0 12 2 8- 0 8- 0 6

摘　　要：采用直流电弧等离子体法 ,分别在 1个大气压的H2 +Ar和CH4+He混和气氛中制备了Fe、Ni、Fe-Ni合金磁性超微粒子 (UFP)。利用Fe、Ni、Fe-Ni合金超微粒子 ,选择适当的表面活性剂和载液 ,制备了高粘度磁性液体(ML) ,常温 (2 5℃ )粘度为 (2 6～ 6 0 )× 10 5mPa·s,高温 (85℃ )粘度为 (1 0～ 3 2 )× 10 5mPa·s,室温下饱和磁化强度为FeML 2 4 0 8～ 6 8 0 0Am2 /kg,NiML 10 19～ 17 83Am2 /kg,Fe-NiML 2 6 2 1～ 75 13Am2Ultrafine Fe, Ni and Fe-Ni particles were prepared by DC electric are plasma method in a mixture of (H 2+Ar) or (CH 4+He) atmosphere Magnetic liquid with high viscosity were produced by using the components of ultrafine metal particles, surfactant and carrying liquid The viscosity of magnetic liquid was in the range( 2 6～6 0)×10 5mPa·s at 25℃ and (1 0～3 2)×10 5mPa·s at 85℃ The saturated magnetization intensity were FeML 24 08～68 00Am 2/kg, NiML 10 19～17 83 Am 2/kg, Fe-NiML 26 21～75 13 Am 2/kg at room temperature

关 键 词：制备 超微粒子 磁性液体 粘度 饱和磁化强度 

分 类 号：TB381[一般工业技术—材料科学与工程]