Solvothermal Synthesis and Crystal Structure of a Novel Inorganic-Organic Hybrid Material, Fe_2O(OH)(C_5H_4NCOO)SO_4  

作　　者：郭洪猷 李增和 李秀艳 张长远 王如骥 

机构地区：[1]Department of Chemistry,Beijing University of Chemical Technology [2]Department of Chemistry,Tsinghua University

出　　处：《Chinese Journal of Chemistry》2003年第4期466-470,共5页中国化学（英文版）

摘　　要：A novel inorganic organic hybrid material, Fe 2O(OH)(C 5H 4 ~NCOO)SO 4 was synthesized via solvothermal route using a reaction of FeCl 3·6H 2O, KCNS, and 4 cyanopyridine in aqueous solution of H 2O 2 and ethanol at 130 ℃ for 3 d. The compound crystallized in monoclinic space group P 2 1, with cell parameters a =0 73850(15) nm, b =0 65100(13) nm, c =1 0546(2) nm, β =90 36(3)°, V =0 50700(18) nm 3 and Z =2. The structure is constructed with inorganic layered [Fe 2O(OH)SO 4] + cations linked by organic (C 5H 4NCOO) - anions. The compound is thermally stable up to approximately 240 ℃.A novel inorganic organic hybrid material, Fe 2O(OH)(C 5H 4 ~NCOO)SO 4 was synthesized via solvothermal route using a reaction of FeCl 3·6H 2O, KCNS, and 4 cyanopyridine in aqueous solution of H 2O 2 and ethanol at 130 ℃ for 3 d. The compound crystallized in monoclinic space group P 2 1, with cell parameters a =0 73850(15) nm, b =0 65100(13) nm, c =1 0546(2) nm, β =90 36(3)°, V =0 50700(18) nm 3 and Z =2. The structure is constructed with inorganic layered [Fe 2O(OH)SO 4] + cations linked by organic (C 5H 4NCOO) - anions. The compound is thermally stable up to approximately 240 ℃.

关 键 词：inorganic  organic hybrid material ferric isonicotinate  sulphate solvothermal synthesis crystal structure 

分 类 号：O627[理学—有机化学]