聚氨酯丙烯酸酯作为预聚体的光敏树脂的制备及性能  

Preparation of the photosensitive resin with urethane acrylate as prepolymer and its properties

作　　者：韩文娟[1] 黄笔武[1] 雍涛[1] 谢王付 万时策 

机构地区：[1]南昌大学材料科学与工程学院,江西南昌330031

出　　处：《南昌大学学报（理科版）》2015年第4期363-367,共5页Journal of Nanchang University(Natural Science)

基　　金：江西省自然科学基金资助项目(20142BAB206029)

摘　　要：以六官能度聚氨酯丙烯酸酯(B-618)、三官能度聚氨酯丙烯酸酯(DH-317)、三丙二醇二丙烯酸酯(TPGDA)和1-羟基环己基苯甲酮(Irgacure184)作为组分制备一系列光敏树脂。利用凝胶率测定法对其光敏树脂的光敏性进行了研究。同时,对该光敏树脂的光固化膜进行了力学性能的测试。实验结果表明该光敏树脂的较佳配方为B-618质量分数28%,DH-317质量分数43%,TPGDA质量分数25%和Irgacure184质量分数4%,且固化膜具有较好的柔韧性、冲击强度和拉伸强度。A photosensitive resin was prepared with hexafunctional urethane acrylate (B-618),trifunctional urethane acrylate (DH-317),tripropylene glycol acrylate (TPGDA)and 1-hydroxy cyclohexyl phenyl ke-tone (Irgacure184).The photosensitive property of the photosensitive resin was investigated by utilizing the gel yield method.Meanwhile,the mechanical properties of the UV-cured films were studied.The results showed that the optimum formulation was B-618 mass factor was 28%,DH-317 mass factor was 43%, TPGDA mass factor was 25% and Irgacure184 mass factor was 4%,and the flexible,impact strength and tensile strength of the UV-cured films were good.

关 键 词：紫外光固化 聚氨酯丙烯酸酯 预聚物 性能 

分 类 号：TQ320.1[化学工程—合成树脂塑料工业]