聚4-重氮基苯乙烯与聚苯乙烯磺酸钠的自组装  

SELF-ASSEMBLY OF POLY(4-DIAZONIUM STYRENE) AND POLY(SODIUMSULFONATE STYRENE)

作　　者：杨朝晖[1] 江玮[1] 曹维孝[1] 

机构地区：[1]北京大学化学与分子工程学院,北京100871

出　　处：《高分子学报》2003年第3期442-444,共3页Acta Polymerica Sinica

基　　金：国家自然科学基金 (基金号 2 0 2 740 0 2和 5 0 1730 0 2 )资助项目

摘　　要：The self-assembly between poly(4-diazonium styrene) (PDS) and poly(sodiumsulfonate styrene)(PSS) was investigated.The mutilayer ult ra thin films were fabricated layer-by-layer successfully from PDS and PSS.Af ter heating for 10 min at 70℃ the multilayer film became very stable towards po lar solvents.No considerable changes were observed for the heated film soaked i n DMF (20℃) for 48 h,while the unheated film almost destroyed at same conditio n.The dramatic improvement in stability of the film towards polar solvents shou ld be attributed to the conversion of bonds between the layers of the film from ionic bond to covalent bond under heating.Y(4 DIAZONIUMSTYRENE)ANDPOLY(SODIUMSULFONATESTYRENE)YANGZhaohui,JIANGWei,CAOWeixiao(CollegeofChemistryandMolecularEngineering ,PekingUniversity ,Beijing　 10 0 871)Abstract　Theself assemblybetweenpoly( 4 diazoniumstyrene) (PDS)andpoly(sodiumsulfonatestyrene) (PSS)wasinvestigated .Themutilayerultrathinfilmswerefabricatedlayer by layersuccessfullyfromPDSandPSS .Afterheatingfor 1 0minat 70℃themultilayerfilmbecameverystabletowardspolarsolvents.NoconsiderablechangeswereobservedfortheheatedfilmsoakedinDMF ( 2 0℃ )for48h ,whiletheunheatedfilmalmostdestroyedatsamecondition.Thedramaticimprovementinstabilityofthefilmtowardspolarsolventsshouldbeattributedtotheconversionofbondsbetweenthelayersofthefilmfromionicbondtocovalentbondunderheating .Keywords　Poly( 4 diazoniumstyrene) 。The self-assembly between poly(4-diazonium styrene) (PDS) and poly(sodiumsulfonate styrene)(PSS) was investigated.The mutilayer ult ra thin films were fabricated layer-by-layer successfully from PDS and PSS.Af ter heating for 10 min at 70℃ the multilayer film became very stable towards po lar solvents.No considerable changes were observed for the heated film soaked i n DMF (20℃) for 48 h,while the unheated film almost destroyed at same conditio n.The dramatic improvement in stability of the film towards polar solvents shou ld be attributed to the conversion of bonds between the layers of the film from ionic bond to covalent bond under heating.Y(4 DIAZONIUMSTYRENE)ANDPOLY(SODIUMSULFONATESTYRENE)YANGZhaohui,JIANGWei,CAOWeixiao(CollegeofChemistryandMolecularEngineering ,PekingUniversity ,Beijing　 10 0 871)Abstract　Theself assemblybetweenpoly( 4 diazoniumstyrene) (PDS)andpoly(sodiumsulfonatestyrene) (PSS)wasinvestigated .Themutilayerultrathinfilmswerefabricatedlayer by layersuccessfullyfromPDSandPSS .Afterheatingfor 1 0minat 70℃themultilayerfilmbecameverystabletowardspolarsolvents.NoconsiderablechangeswereobservedfortheheatedfilmsoakedinDMF ( 2 0℃ )for48h ,whiletheunheatedfilmalmostdestroyedatsamecondition.Thedramaticimprovementinstabilityofthefilmtowardspolarsolventsshouldbeattributedtotheconversionofbondsbetweenthelayersofthefilmfromionicbondtocovalentbondunderheating .Keywords　Poly( 4 diazoniumstyrene) ,Poly(sod

关 键 词：聚4-重氮基苯乙烯 聚苯乙烯磺酸钠 自组装 超薄膜 LB膜 交联结构 

分 类 号：O631[理学—高分子化学]