新型磷铝酸盐水泥与硅酸盐水泥粘结界面的研究  

The Interface Between Phosphoaluminate Cement and Silicate Cement

作　　者：张爱娟[1] 胡佳山[1] 李仕群[1] 

机构地区：[1]济南大学材料科学与工程学院,山东济南250022

出　　处：《济南大学学报（自然科学版）》2003年第2期100-103,共4页Journal of University of Jinan(Science and Technology)

基　　金：973国家重点基础研究发展规划项目资助 (编号2 0 0 1CB610 70 2 -3 )

摘　　要：通过测定界面的抗拉、抗折、剪切强度 ,系统地研究了磷铝酸盐水泥与硅酸盐水泥试样界面的粘结性能 ,并对“磷 -硅” ,“硅 -硅”界面进行比较 ;同时借助于X射线衍射、扫描电镜和能谱等测试技术 ,初步分析了界面区的粘结机理。试验结果表明 :“磷 -硅”界面具有良好的粘结性能 。According to the pull resistance,bending resistance,shearing strength of the interface,the text studies the property of the interface between phosphoaluminate cement and silicate cement systematically and compares the'phosphoaluminate silicate','silicon silicon'interface as well.At the same time,the cling mechanism of the interface is analysed by the testing technology such as XRD,SEM and ES.The result of the experiment shows that the cling property of'phosphoaluminate silicate'is good and is the result of the physical combination and chemical combination act together.

关 键 词：磷铝酸盐水泥 粘结界面 机理分析 

分 类 号：TU502.6[建筑科学—建筑技术科学]