Effect of Graft Yield on the Thermo-Responsive Permeability Through Porous Membranes with Plasma-Grafted Poly(N-isopropylacrylamide)Gates  

作　　者：褚良银 朱家骅 陈文梅 NIITSUMA Takuya YAMAGUCHI Takeo NAKAO Shin-ichi 

机构地区：[1]School of Chemical Engineering,Sichuan University,Chengdu 610065,China [2]Department of Chemical System Engineering,University of Tokyo,113-8656,Japan

出　　处：《Chinese Journal of Chemical Engineering》2003年第3期269-275,共7页中国化学工程学报（英文版）

基　　金：Supported by the National Natural Science Foundation of China(No.29876022).

摘　　要：The effect of graft yield on both the thermo-responsive hydraulicpermeability and the therrno-responsive diffusional permeability through porous membranes withplasma-grafted poly(N-isopropylacrylamide) (PNIPAM) gates was investigated. Both thermo-responsiveflat membranes and core-shell microcapsule membranes with a wide range of graft yield of PNIPAM wereprepared using a plasma-graft pore-filling polymerization method. The grafted PNIPAM was formedhomogeneously throughout the entire thickness of both the flat polyethylene membranes and themicrocapsule polyamide membranes. Both the hydraulic permeability and the diffusional permeabilitywere heavily dependent on the PNIPAM graft yield. With increasing the graft yield, the hydraulicpermeability (water flux) decreases rapidly at 25℃ because of the decrease of the pore size;however, the water flux at 40℃ increases firstly to a peak because of the increase ofhydrophobicity of the pore surface, and then decreases and finally tends to zero because of the poresize becoming smaller and smaller. For the diffusional permeability, the temperature showsdifferent effects on the diffusional permeability coefficients of solutes across the membranes. Whenthe graft yield was low, the diffusional coefficient of solute across the membrane was higher attemperature above the lower critical solution temperature (LCST) than that below the LCST; however,when the graft yield was high, the diffusional coefficient was lower at temperature above the LCSTthan that below the LCST. It is very important to choose or design a proper graft yield of PNIPAMfor obtaining a desired thermo-responsive 'on/off' hydraulic or diffusional permeability.The effect of graft yield on both the thermo-responsive hydraulic permeability and the thermo-respousive diffusional permeability through porous membranes with plasma-grafted poly(N-isopropylacrylamide) (PNIPAM)gates was investigated. Both thermo-respousive flat membranes and core-shell microcapsule membranes with a wide range of graft yield of PNIPAM were prepared using a plasma-graft pore-filling polymerization method. The grafted PNIPAM was formed homogeneously throughout the entire thickness of both the fiat polyethylene membranes andthe microcapsule polyamide membranes. Both the hydraulic permeability and the diffusional permeability were heavily dependent on the PNIPAM graft yield. With increasing the graft yield, the hydraulic permeability (water flux) decreases rapidly at 25℃ because of the decrease of the pore size; however, the water flux at 40℃ increases firstly to a peak because of the increase of hydrophobicity of the pore surface, and then decreases and finally tends to zero because of the pore size becoming smaller and smaller. For the diffusional permeability, the temperature shows different effects on the diffusional permeability coefficients of solutes across the membranes. When the graft yield was low, the diffusional coefficient of solute across the membrane was higher at temperature above the lower critical solution temperature (LCST) than that below the LCST; however, when the graft yield was high, the diffusional coefficient was lower at temperature above the LCST than that below the LCST. It is very important to choose or design a proper graft yield of PNIPAM for obtaining a desired thermo-respousive 'on/off' hydraulic or ditfusional permeability.

关 键 词：thermo-responsive membrane poly(N-isopropylacrylamide) plasma-graftpore-filling polymerization graft yield hydraulic permeability diffusional permeability 

分 类 号：TQ316.3[化学工程—高聚物工业]