GRAFTING OF SULFOBETAINE ONTO A POLYURETHANE SURFACE TO IMPROVE BLOOD COMPATIBILITY  

作　　者：林思聪 

机构地区：[1]Research Center of Surface and Interface Chemical and Engineering Technology Nanjing University,Nanjing 210093, China

出　　处：《Chinese Journal of Polymer Science》2003年第4期419-426,共8页高分子科学（英文版）

基　　金：Project of 973 State key Foundation Research and Development (No. 1999064705) sponsored and supported by Ministry of Science and Technology of China.

摘　　要：On the molecular level, it is believed that polymers containing zwitterionic structures should be compatible withblood. In this work polyurethane films were grafted with sulfobetaine by a three-step procedure. In the first step, the films'surfaces were treated with hexamethylene diisocyanate (HDI) in toluene at 50℃ in the presence of di-n-butyl tin dilaurate(DBTDL) as a catalyst. The extent of the reaction was monitored by ATR-IR spectra; a maximum number of free NCOgroups was obtained after a reaction time of 90 min. In the second step, the hydroxyl groups of N,N-dimethylethylethanolamine (DMEA) were allowed to react in toluene with NCO groups bound on the surface. In the thirdstep, sulfobetaines were formed on the surface through the ring-opening reaction between tertiary amine of DMEA and 1,3-propanesultone (PS). The surfaces of the films were characterized by ATR-IR and XPS showing that the grafted surfaceswere composed of sulfobetaine. The results of the contact angle measurement show that the surface was strongly hydrophilic.The platelet adhesion test demonstrated that the films grafted with sulfobetaine have excellent blood compatibility.On the molecular level, it is believed that polymers containing zwitterionic structures should be compatible withblood. In this work polyurethane films were grafted with sulfobetaine by a three-step procedure. In the first step, the films'surfaces were treated with hexamethylene diisocyanate (HDI) in toluene at 50℃ in the presence of di-n-butyl tin dilaurate(DBTDL) as a catalyst. The extent of the reaction was monitored by ATR-IR spectra; a maximum number of free NCOgroups was obtained after a reaction time of 90 min. In the second step, the hydroxyl groups of N,N-dimethylethylethanolamine (DMEA) were allowed to react in toluene with NCO groups bound on the surface. In the thirdstep, sulfobetaines were formed on the surface through the ring-opening reaction between tertiary amine of DMEA and 1,3-propanesultone (PS). The surfaces of the films were characterized by ATR-IR and XPS showing that the grafted surfaceswere composed of sulfobetaine. The results of the contact angle measurement show that the surface was strongly hydrophilic.The platelet adhesion test demonstrated that the films grafted with sulfobetaine have excellent blood compatibility.

关 键 词：POLYURETHANE SULFOBETAINE Surface modification Platelet adhesion Nonthrombogenic biomaterials 

分 类 号：TQ316.6[化学工程—高聚物工业]