PARTICLE MORPHOLOGY OF POLY(VINYL CHLORIDE)RESIN PREPARED BY SUSPENDED EMULSION POLYMERIZATION  

作　　者：包永忠 

机构地区：[1]State Key Laboratory of Polymer Engineering Zhejiang University Hangzhou 310027, China

出　　处：《Chinese Journal of Polymer Science》2003年第4期447-452,共6页高分子科学（英文版）

基　　金：The project is supported by the National Natural Science Foundation of China (No. 29906009)

摘　　要：Suspended emulsion polymerization was used to prepare poly(vinyl chloride) (PVC) resin. Fine PVC particleswere formed at low polymerization conversions. The amount of fine panicles decreases as conversion increases anddisappears at conversions greater than 30%. Scanning electron micrographs show that PVC grains are composed of looselycoalesced primary particles, especially for PVC resins prepared in the presence of poly(vinyl alcohol) dispersant. The size ofprimary particles increases and porosity decreases with the increase of conversion. In view of the particle features of PVCresin, a particle formation mechanism including the formation of primary particles and grains is proposed. The formationprocess of primary particles includes the formation of particle nuclei, coalescence of particle nuclei to form primary particles,and growth of primary particles. PVC grains are formed by the coagulation of primary particles. The loose coalescence ofprimary particles is caused by the colloidal stability of primary particles and the low swelling degree of vinyl chloride in the primary particles.Suspended emulsion polymerization was used to prepare poly(vinyl chloride) (PVC) resin. Fine PVC particleswere formed at low polymerization conversions. The amount of fine panicles decreases as conversion increases anddisappears at conversions greater than 30%. Scanning electron micrographs show that PVC grains are composed of looselycoalesced primary particles, especially for PVC resins prepared in the presence of poly(vinyl alcohol) dispersant. The size ofprimary particles increases and porosity decreases with the increase of conversion. In view of the particle features of PVCresin, a particle formation mechanism including the formation of primary particles and grains is proposed. The formationprocess of primary particles includes the formation of particle nuclei, coalescence of particle nuclei to form primary particles,and growth of primary particles. PVC grains are formed by the coagulation of primary particles. The loose coalescence ofprimary particles is caused by the colloidal stability of primary particles and the low swelling degree of vinyl chloride in the primary particles.

关 键 词：Suspended emulsion polymerization Vinyl chloride Particle size distribution MORPHOLOGY Particle formation mechanism 

分 类 号：TQ316.334[化学工程—高聚物工业]