COPET/PET海岛复合纤维的碱减量处理及其对纤维结构的影响  

Causticization for the COPET/PET Sea-island Composite Fiber and its Influence on Fiber Structure

作　　者：郭静[1] 徐德增[1] 赵军 周峰 

机构地区：[1]大连轻工业学院,116034 [2]辽阳天利海岛纤维有限公司,111000

出　　处：《合成纤维》2003年第4期27-28,共2页Synthetic Fiber in China

摘　　要：采用1％的NaOH溶液,在100℃条件下,对COPET/PET海岛复合纤维进行碱处理,考察了碱处理时间对碱减率和纤维开纤情况的影响,发现随碱处理时间延长,纤维碱减率增大,开纤效果好。综合纤维的碱减率和开纤情况认为,在给定条件下,40分钟的碱处理条件较优。The COPET/PET sea-island composite fiber is treated with 1 % NaOH solution under 100℃. The relationship between the alkali treatment time and the levels of weight loss of and the state of splitting is investigated. The results show that the levels of weight loss increase as the alkali treatment time increasing, and the state of splitting is better. According to the levels of weight loss and the state of splitting, 40 minutes is better condition.

关 键 词：COPET/PET海岛复合纤维 碱减量处理 纤维结构 开纤 