酚酞环氧树脂的合成研究  

Study on synthesis of phenolphthalein epoxy resin

作　　者：翟春[1] 杨高文[1] 徐刚[2] 

机构地区：[1]常熟理工学院化学科学与技术系,江苏常熟215500 [2]江西师范大学化学科学学院,江西南昌330027

出　　处：《应用化工》2003年第4期47-50,共4页Applied Chemical Industry

摘　　要：在碱金属盐K2CO3/H2O催化下,由酚酞和环氧氯丙烷缩聚制得了低分子量酚酞环氧树脂。用红外光谱表征了其分子结构,测定了酚酞环氧树脂的环氧值。讨论了单体的摩尔比、催化剂用量、水含量及反应温度对产物环氧值的影响。结果表明:在实验范围内,改变酚酞与环氧氯丙烷的摩尔比(1∶10～1∶4)或酚酞与催化剂的摩尔比(1∶2～1∶1),均可得到低分子量的酚酞环氧树脂。A series of low molecular weight phenolphthalein epoxy resins(Ⅰ) have been prepared from phenolphthalein and epichlorohydrin using K2CO3/H2O as catalysts. The structure of I are characterized by IR. The epoxy value(E) are also measured. The effects of the molar ratios of monomer, reaction temperature, contents of the catalysts and water on the E value are tested.The results showed that the I can be obtained in a wide range of molar ratio of phenolphthalein to epichlorohydrin or phenophthalein to the catalyst K2CO3. 

关 键 词：酚酞环氧树脂 碱金属碳酸盐 合成 

分 类 号：O633.13[理学—高分子化学]