等离子喷涂参数对Ta/W/Sn复合涂层组织性能的影响(英文)  

Effects of Plasma Spray Parameters on Structure of Ta/W/Sn Multilayer Coatings

作　　者：蒋驰[1] 周晋林[1] 肖云峰[1] 税毅[1] 王述刚[1] 刘春荣[1] 

机构地区：[1]中国工程物理研究院,四川绵阳621900

出　　处：《稀有金属材料与工程》2003年第7期554-557,共4页Rare Metal Materials and Engineering

基　　金：SupportedbytheFoundationofChinaAcademyofEngineeringPhysics(2001.0331)

摘　　要：采用等离子喷涂方法在LY12铝上制备了Ta/W/Sn复合涂层。研究了各种工艺参数对涂层材料熔化程度和沉积效率的影响。采用扫描电子显微镜观察了复合涂层的表面及界面,精密机械天平称量涂层的增重,力学拉伸机测量涂层的抗拉结合强度,能谱和化学方法分析涂层的化学成分。结果表明,等离子喷涂工艺可以制作组织致密、厚度均匀的Ta/W/Sn复合涂层;喷涂功率和送粉速率对材料的熔化状态影响较大,在特定喷距范围内喷距的影响则较小。Ta/W/Sn multilayer coatings were made on LY12 aluminium substrate by plasma spray. Effect of various parameters on the melting degree and deposition efficiency of feedstock has been investigated. The surface and the interfaces morphology of the multilayer coatings were observed using scanning electron microscopy. The weight gain of the coatings was weighed using precision mechanical balance. The-tensile strength of the multilayer was determinated by mechnical testing machine. The chemical composition of these coatings was seperately obtained using auger energy spectrum and chemical analysis. The result shows that Ta/W/Sn multilayer coatings with fine structure and uniform thickness could be prepared by plasma spray processes. The degree of the powders melting is much affected by spray power and spray rate, and does not vary much with spray distance within the specific range.

关 键 词：等离子喷涂 复合涂层 LY12铝 

分 类 号：TG174.442[金属学及工艺—金属表面处理]