Fe-Co-Si-Cu热电材料的输运特性(英文)  

Transport Properties of Fe-Co-Si-Cu Thermoelectric Alloys

作　　者：李伟文[1] 赵新兵[1] 朱铁军[1] 曹高劭[1] 

机构地区：[1]浙江大学硅材料国家重点实验室,浙江杭州310027

出　　处：《稀有金属材料与工程》2003年第8期621-623,共3页Rare Metal Materials and Engineering

基　　金：SupportedbytheNationalNaturalScienceFoundationofChina(NSFC59971044)

摘　　要：采用真空悬浮熔炼和真空退火方法制备了Fe1-xCoxSi2-0.1at%Cu热电材料。试样的微观组织中包含大量尺寸在1μm左右的小孔和一些裂纹。输运特性测量结果表明,550K时掺杂载流子的热激发达到饱和,700K以上发生本征激发现象。实验发现Co的最佳掺杂量为1at%左右,名义组成为Fe0.97Co0.03Si2-0.1at%Cu的试样的热电性能最好。The microstructure and transport properties of the levitation-melting thermoelectric alloys F1-xCoxSi2-O. 1 at% Cu were examined. Their microstructures were found to consist of many grains and crystal boundaries in a B-FeSi2 matrix. The alloy Fe0.97Co0.03Si2-O. 1 at% Cu annealed for 24 h at 1 070K was found to have excellent transport properties. It is suggested that doping with 1.0 at% (x = 0.03) of cobalt can significantly improve the thermoelectric properties of Fe1-xCoxSi2-O. 1 at% Cu.