涤纶有光异形全拉伸丝工艺探讨  

Technology discussion on PET fiber bright profiled FDY

作　　者：王石泉 沈华 

机构地区：[1]湖南荣通化纤有限公司,湖南湘潭411101 [2]深圳市华联控股股份有限公司,广东深圳518031

出　　处：《聚酯工业》2003年第4期42-44,共3页Polyester Industry

摘　　要：介绍在切片纺FDY生产线上开发55dtex有光三叶异形全拉伸丝。预结晶温度120～150℃,时间20min,155～170℃下干燥8h,干切片中w(H2O)<30×10-6。增大螺杆1—4区的温度梯度,出口温度296～298℃。冷却风速0.32～0.36m/s,风温20～25℃,调整油轮转速和与丝束的包角控制纺丝张力。纺丝速度4500～4800m/min,热辊拉伸倍数2.50～2.90,第一、二热辊温度为85～90℃、140℃。The development condition of 55 dtex bright trilobal profiled FDY on chip spinning FDY production line is introduced.The precrystallization temperature is 120～150 ℃,the precrystallization time is 20 min,the mass fraction of water in dry chip is less than 30×10-6 when drying out for 8h at the temperature of 155～170 ℃.The temperature gradient of 1-4 zone of screw extruder is increased,the exit temperature is 296～298 ℃,the cooling speed is 0.32～0.36 m/s,the wind temperature is 20～25 ℃,the wrapping angle between the rotation speed of oiling roller and tow line is adjusted to control the spinning tension.The spinning speed is 4 500～4 800 m/min,the stretching ratio of hot roller respectively is 2.50～2.90,the temperature of the first and second hot roller is 85～90 ℃ and 140 ℃.

关 键 词：涤纶 有光三叶异形丝 全拉伸丝工艺 纺丝工艺 卷绕工艺 

分 类 号：TQ342.2[化学工程—化纤工业] TQ340.651