纳米CaCO_3-PVC增塑糊流变性能的研究  

Rheology of nano-calcium carbonate/PVC paste resin

作　　者：邹海魁[1] 陈建峰[1] 刘润静[1] 王玉红[1] 王国全[2] 

机构地区：[1]北京化工大学教育部超重力工程研究中心,北京100029 [2]北京化工大学材料科学与工程学院,北京100029

出　　处：《北京化工大学学报（自然科学版）》2002年第3期5-8,共4页Journal of Beijing University of Chemical Technology(Natural Science Edition)

基　　金：国家"863"计划资助项目(863-715-009-0080)

摘　　要：主要研究了改性纳米CaCO3填充PVC糊树脂的流变性能。结果表明,改性纳米CaCO3/PVC增塑糊具有明显的切应力变稀性能和触变性能,与英国ICI公司生产的改性纳米CaCO3相比,北京化工大学超重力工程研究中心制备的改性纳米CaCO3填充的PVC增塑糊在高剪切速率下粘度相当的情况下低剪切速率时的粘度更高,环面积大一倍左右,具有更好的触变性能。Rheology of PVC (poly(vinyl chloride)) paste resin filled with nano-sized calcium carbonate was investigated . It is found that the presence of nano-sized calcium carbonate has significantly improved the quality of thinning and thixotropy. The performance of commercially available nano-sized calcium carbonate (ICI, product coded winnofil) was compared with that of nano-sized calcium carbonate prepared by high gravity reactive precipitation technology developed by the authors. While both products have similar viscosity at a high shear rate, the latter shews to have lower viscosity at a low shear rate, which is desired for PVC paste resin with better thixotropy.

关 键 词：改性纳米CACO3 PVC糊树脂 切力变稀性能 触变性能 粘度 

分 类 号：TQ325.3[化学工程—合成树脂塑料工业]