一种新型高强韧性耐磨钢的纳米结构原子像及其性能  

Nanostructure atomic image and mechanical properties of a novel wear resistance steel with high strength and toughness

在线阅读下载全文

作  者:伦宁[1] 秦超[1] 李凤照[1] 

机构地区:[1]山东大学材料科学与工程学院材料表征和分析中心,山东济南250061

出  处:《山东大学学报(工学版)》2003年第4期367-371,共5页Journal of Shandong University(Engineering Science)

基  金:山东省自然科学基金资助项目 (Y2 0 0 1F15 )

摘  要:研制的新型高强韧性耐磨钢 ,铸态空冷及淬火回火处理均可获得细小或隐晶马氏体 ,少量贝氏体和残留奥氏体以及碳化物 .铸态淬火回火处理样品的U 型缺口冲击韧度аk =38~ 5 0J cm2 ,无缺口冲击韧度аk =14 0~ 2 90J cm2 ,HRC =5 3~ 5 6 ;锻后淬火回火处理样品U 型缺口冲击韧度аk=5 0~ 70J cm2 ,HRC =5 2~ 5 4 ,抗拉强度σb=185 0~ 2 0 0 0Mpa .所研制钢的冲击韧度较相近成分的贝氏体钢提高 4 0 % .采用高分辨电镜对新型钢的纳米结构原子像进行了观察 ,确定了贝氏体铁素体亚片条尺寸 .The microstructures of medium carbon wear resistance steel after quenching and tempering are martensite and small amount of bainite, retained austenite and carbide. The impact toughness with U notch as cast afrer air cooled was within 38~50?J/cm 2, and the impact toughness without notch was 140~290?J/cm 2. with hardness HRC =53~56; while in forged stage, their hardness was HRC =52~54, the impact toughness with U notch was 50~70?J/cm 2, and the tensile strength σ b =1850~2000?Mpa. The impact toughness of the studied medium carbon low alloy steel containing martensite, bainite and small amount of retained austenite is 40% higher than that of normal Mn B and Mn Si B bainitic steels. The nanostructure atomic image of the steel was observed with high resolution electron microscopy and the sizes of subplate of bainitic ferrite were determined.

关 键 词:高强韧钢 冲击韧度 马氏体 贝讼体 原子像 

分 类 号:TG113[金属学及工艺—物理冶金]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象