Cathodic electrolysis method of depositing cerium conversion films on industrial pure aluminum  

作　　者：ZHANG Wei, LI Jiuqing, WU Yinshun, SHEN Defeng, and HE JianpingDepartment of Surface Science & Corrosion Engineering, University of Science and Technology Beijing, Beijing 100083, China 

出　　处：《Rare Metals》2002年第2期95-100,共6页稀有金属（英文版）

基　　金：financially supported by the National Natural Science Foundation of China (No.59771067)

摘　　要：Two two-step techniques, called TS2/TS7 and TS3/TS7, respectively,have been developed to form cerium conversion films on the surface ofindustrial pure aluminum. The tested material was cathodicallyelectrolyzed in the al- kaline solution containing cerium salt, anduniform films containing cerium were obtained after the two-steptreatment. It is found that the films obtained by TS2/TS7 and TS3/TS7techniques are about 4.0 and 3.0 um in thickness, respectiv- Ely. Thematerial has better corrosion resistance in the chloride solutionafter the two-step electrolysis treatent compar- Ed with the one-steptreated and naked specimens.Two two-step techniques, called TS2/TS7 and TS3/TS7, respectively,have been developed to form cerium conversion films on the surface ofindustrial pure aluminum. The tested material was cathodicallyelectrolyzed in the al- kaline solution containing cerium salt, anduniform films containing cerium were obtained after the two-steptreatment. It is found that the films obtained by TS2/TS7 and TS3/TS7techniques are about 4.0 and 3.0 um in thickness, respectiv- Ely. Thematerial has better corrosion resistance in the chloride solutionafter the two-step electrolysis treatent compar- Ed with the one-steptreated and naked specimens.

关 键 词：aluminum alloy rare earth conversion film cathodic electrochemicaldeposition 

分 类 号：TG174.4[金属学及工艺—金属表面处理]