0Cr13Al/20R复合板焊接接头的组织与性能  

Welding Joint Structure and Performance of 0Cr13Al/20R Composite Plate

作　　者：肖宏滨[1] 辛选荣[1] 祝要民[1] 李炎[1] 

机构地区：[1]洛阳工学院材料科学与工程系,河南洛阳471003

出　　处：《洛阳工学院学报》2002年第4期38-40,共3页Journal of Luoyang Institute of Technology

基　　金：洛阳工学院科研基金资助项目 (942 0 2 0 4)

摘　　要：对 0Cr13Al 2 0R复合板实际生产中的对接接头性能进行了系统的试验 ,采用电镜等手段就其焊接接头的界面微观组织进行了分析研究 ,探讨了焊接工艺规范与组织、性能之间的关系。试验结果表明 ,本试验所采用的焊接材料和工艺规范可获得性能良好的对接接头 。On the basis of the practical production,the butt welding joint performances of 0Cr13Al/20R composite plate are tested systematically. By means of the electron microscope,the boundary microscopic structure of the welding joint is studied.Meanwhile,the relationship between the norm of welding techniqe and the structure and the performance is investigated.The experimental results show,under this test condition of the welding material and technology,the butt welding joint performance is well and the boundary microscopic structure is normal.

关 键 词：0Cr13Al/20R复合板 焊接接头 微观组织 爆炸焊接 显微硬度 

分 类 号：TG457.1[金属学及工艺—焊接] TG45