用于循环冷却水处理的新型阻垢剂的合成及性能研究  

RESEARCH ON SYNTHESIS AND PERFORMANCE OF A NEW SCALE INHIBITOR FOR CYCLE-COOLING WATER SYSTEM

作　　者：吴兵[1] 徐瑞银[2] 何绪文[2] 卢桂兰[1] 李发生[1] 

机构地区：[1]中国环境科学研究院,北京100012 [2]北京科技大学,北京100083

出　　处：《环境工程》2003年第5期13-15,共3页Environmental Engineering

摘　　要：以马来酸和丙烯酸为原料 ,添加一定比例的过氧化物和次亚磷酸钠 ,合成了一种水溶性共聚物阻垢剂。当马来酸与丙烯酸的摩尔比为 1∶4 ,过氧化物的添加量为 10 % ,次亚磷酸钠的添加量为 2 0 %时 ,反应温度为 85～ 90℃ ,反应时间为 4h时 ,制备的阻垢剂性能良好。当其在模拟冷却水中的加入量为 15× 10 - 6 时 ,静态阻垢率达到 96 4 6 % ,静态缓蚀率为 14 5 6 %。A kind of water soluble scale inhibitor is synthesized based on maleic and acrylic acid and by adding peroxide and sodium hypophosphite.The reaction conditions were optimized as follows:temperature=85～90 ℃,and reaction time=4 hr,the molar ratio of maleic acid to acrylic acid=1∶4,the amount of peroxide=10% and the amount of hypophosphite=20%.When 15×10 -6 of the prepared polymer compound is used for simulated cooling water,static scale inhibiting ratio can reach 96.46% and static corrosion delaying ratio is 14.56%.

关 键 词：循环冷却水 阻垢剂 性能 马来酸 丙烯酸 水处理 

分 类 号：X703[环境科学与工程—环境工程]