Enhancement of bimetallic Fe-Mn/CNTs nano catalyst activity and product selectivity using microemulsion technique  

作　　者：Zahra Zolfaghari Ahmad Tavasoli Saber Tabyar Ali Nakhaei Pour 

机构地区：[1]School of Chemistry,College of Science,University of Tehran [2]School of Chemistry,Ferdowsi University of Mashhad

出　　处：《Journal of Energy Chemistry》2014年第1期57-65,共9页能源化学（英文版）

摘　　要：Bimetallic Fe-Mn nano catalysts supported on carbon nanotubes(CNTs) were prepared using microemulsion technique with water-to-surfactant ratios of 0.4-1.6. The nano catalysts were extensively characterized by different methods and their activity and selectivity in Fischer-Tropsch synthesis(FTS) have been assessed in a fixed-bed microreactor. The physicochemical properties and performance of the nanocatalysts were compared with the catalyst prepared by impregnation method. Very narrow particle size distribution has been produced by the microemulsion technique at relatively high loading of active metal. TEM images showed that small metal nano particles in the range of 3–7 nm were not only confined inside the CNTs but also located on the outer surface of the CNTs. Using microemulsion technique with water to surfactant ratio of0.4 decreased the average iron particle sizes to 5.1 nm. The reduction percentage and dispersion percentage were almost doubled. Activity and selectivity were found to be dependent on the catalyst preparation method and average iron particle size. CO conversion and FTS rate increased from 49.1% to 71.0% and 0.144 to 0.289 gHC/(gcat h), respectively. While the WGS rate decreased from 0.097 to 0.056 gCO2/(gcat h). C5+liquid hydrocarbons selectivity decreased slightly and olefins selectivity almost doubled.Bimetallic Fe-Mn nano catalysts supported on carbon nanotubes(CNTs) were prepared using microemulsion technique with water-to-surfactant ratios of 0.4-1.6. The nano catalysts were extensively characterized by different methods and their activity and selectivity in Fischer-Tropsch synthesis(FTS) have been assessed in a fixed-bed microreactor. The physicochemical properties and performance of the nanocatalysts were compared with the catalyst prepared by impregnation method. Very narrow particle size distribution has been produced by the microemulsion technique at relatively high loading of active metal. TEM images showed that small metal nano particles in the range of 3–7 nm were not only confined inside the CNTs but also located on the outer surface of the CNTs. Using microemulsion technique with water to surfactant ratio of0.4 decreased the average iron particle sizes to 5.1 nm. The reduction percentage and dispersion percentage were almost doubled. Activity and selectivity were found to be dependent on the catalyst preparation method and average iron particle size. CO conversion and FTS rate increased from 49.1% to 71.0% and 0.144 to 0.289 gHC/(gcat h), respectively. While the WGS rate decreased from 0.097 to 0.056 gCO2/(gcat h). C5+liquid hydrocarbons selectivity decreased slightly and olefins selectivity almost doubled.

关 键 词：Fischer-Tropsch synthesis iron MAGNESIUM MICROEMULSION particle size activity product selectivity 

分 类 号：TQ426[化学工程] TB383.1[一般工业技术—材料科学与工程]