铝基复合材料的Al-Cu合金中间层瞬间液相扩散连接  

Transient liquid phase bonding of aluminium-based metal matrix composite with Al-Cu alloy interlayer

作　　者：刘卫红[1] 孙大谦[1] 贾树盛[1] 邱小明[1] 

机构地区：[1]吉林大学汽车材料教育部重点实验室,长春130025

出　　处：《焊接学报》2003年第5期13-16,共4页Transactions of The China Welding Institution

基　　金：国家教育部基金;国家留学基金委资助项目

摘　　要：采用Al-Cu合金作为中间层研究了铝基复合材料(Al_2O_(3P)/6061Al)瞬间液相扩散连接接头的组织与力学性能。研究结果表明,在Al-Cu/Al_2O_(3P)/6061Al接头中无明显的增强相偏聚区和增强相贫化区,且接头成分分布较为均匀;在Al-Cu合金中间层厚度30μm、连接温度600℃、连接时间30min条件下,接头抗剪强度为130-140MPa,较Cu/Al_2O_(3P)/6061Al接头抗剪强度提高45％。因此,采用Al-Cu中间层是改善铝基复合材料接头力学性能的有效途径。The microstructure and mechanical properties of transient liquid phase bonded aluminium-based metal matrix composite (Al2O3P/6061 Al) joint with Al-Cu alloy interlayer have been investigated. The experimental results show that compared with the joint of Cu interlayer there are not obvious particulate segregation region and denuded particulate region. Cu concentration distribution is more homogeneous, and the shear strength of the joint increases by 45%. It is effective to use Al-Cu alloy interlayer for improving the mechanical property of transient liquid phase bonded aluminium-based metal matrix composite joint.

关 键 词：铝基复合材料 中间层 瞬间液相扩散连接 AL-CU合金 力学性能 

分 类 号：TG457.14[金属学及工艺—焊接] TG453