循环用阀控电池失效模式的研究  

On the failure mode of VRLA batteries

作　　者：吴贤章[1] 胡信国[1] 

机构地区：[1]哈尔滨工业大学应用化学系,黑龙江哈尔滨150001

出　　处：《电池》2003年第5期299-301,共3页Battery Bimonthly

摘　　要：采用孔率测试、X射线衍射、电镜扫描等手段,对循环失效后的活性物质(AM)的成分与结构进行了较深入的研究,分析认为循环使用条件下,电池的失效主要是由正极活性物质(PAM)的软化、脱落所致。The components and structure of failed active material(AM) after cycling were investigated using porosity test,XRD and SEM.It showed that the failure mode of VRLA batteries was the positive active material softening and shedding under the cycling operation condition.

关 键 词：阀控式密封铅酸蓄电池 失效模式 活性物质 循环寿命 

分 类 号：U463.6[机械工程—车辆工程]