Preparation and Properties of Pillared Montmorillonite by Polyhydroxyl-aluminum-manganese Cations  

作　　者：曹明礼 

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2002年第2期43-46,共4页武汉理工大学学报（材料科学英文版）

基　　金：Supported by Foundation for University Key Teacher by the Ministry of Education

摘　　要：Al-Mn-pillared montmorillonite(AMPM) was prepared by using the artificial Na-montmoril-lonite from the Qingfengshan bentonite mine as starting materials mixed with Al-Mn pillaring solutions at different Al/Mn molar ratios (R). The basal spacing and specific surface area of the materials were increased significantly compared with untreated clays. When R = 0.5, the d (001) value and specific surface area of pillared montmoril-lonite were 1.8987 ran and 146.01 m2 g-1, respectively. The thermal stability was determined using calcined tests , X-ray diffraction ( XRD ) analysis, thermal gravimetry and differential thermal analysis (TG - DTA). The materials formed at initial R = 0.5 exhibited a high stability, the basal interlayer spacing was stabilized at 1.7859 nm after calcined for 2 h at 300℃. The adsorption behavior of the materials was studied by adsorption experiments. The results show the AMPM and calcined Al-Mn-pillared montmorillonite ( CAMPM) exhibit a strong capacity of adsorbing the Zn(Ⅱ) in aqueous solution at pH 10.0.Al-Mn-pillared montmorillonite(AMPM) was prepared by using the artificial Na-montmoril-lonite from the Qingfengshan bentonite mine as starting materials mixed with Al-Mn pillaring solutions at different Al/Mn molar ratios (R). The basal spacing and specific surface area of the materials were increased significantly compared with untreated clays. When R = 0.5, the d (001) value and specific surface area of pillared montmoril-lonite were 1.8987 ran and 146.01 m2 g-1, respectively. The thermal stability was determined using calcined tests , X-ray diffraction ( XRD ) analysis, thermal gravimetry and differential thermal analysis (TG - DTA). The materials formed at initial R = 0.5 exhibited a high stability, the basal interlayer spacing was stabilized at 1.7859 nm after calcined for 2 h at 300℃. The adsorption behavior of the materials was studied by adsorption experiments. The results show the AMPM and calcined Al-Mn-pillared montmorillonite ( CAMPM) exhibit a strong capacity of adsorbing the Zn(Ⅱ) in aqueous solution at pH 10.0.

关 键 词：Al-Mn-pillared montmorillonite pillaring solution pofyhydroxyl-aluminum-manganese cations preparation properties 

分 类 号：TQ325[化学工程—合成树脂塑料工业]