Spectral Parameters of Nd^(3+)∶Sr_6YSc(BO_3)_6  

作　　者：林州斌 胡祖树 王国富 

机构地区：[1]Fujian Institute of Research on the Structure of Matter Chines e Academy of Sciences

出　　处：《Journal of Rare Earths》2003年第1期23-25,共3页稀土学报（英文版）

基　　金：NaturalScienceFoundationofFujianProvince (A0 110 0 18)

摘　　要：The crystal Nd 3+∶Sr 6YSc(BO 3) 6 was grown by the top-seeded solution growth method from a Li 6B 4O 9 flux. The s pectral properties of Nd 3+∶Sr 6YSc(BO 3) 6 crystal were investigated. Using Judd-Ofelt theory to ana lyze the optical strength measured in absorption spectrum, the following spectr al parameters were obtained: parameters of oscillator strengths Ω λ are Ω 2=1.194×10 -20 cm2, Ω 4=4.186×10 -20 cm2 and Ω 6=3.3 51×10 -20 cm2. The radiative lifetime is 322 μs, and the fluorescence b ranch ratios were calculated: β 1=0.465, β 2=0.453, β 3=0.079 and β 4=0.004. The results indicate that Nd 3+∶Sr 6YSc(BO 3) 6 c rystal seems to be a potential high-efficient laser material.The crystal Nd 3+∶Sr 6YSc(BO 3) 6 was grown by the top-seeded solution growth method from a Li 6B 4O 9 flux. The s pectral properties of Nd 3+∶Sr 6YSc(BO 3) 6 crystal were investigated. Using Judd-Ofelt theory to ana lyze the optical strength measured in absorption spectrum, the following spectr al parameters were obtained: parameters of oscillator strengths Ω λ are Ω 2=1.194×10 -20 cm2, Ω 4=4.186×10 -20 cm2 and Ω 6=3.3 51×10 -20 cm2. The radiative lifetime is 322 μs, and the fluorescence b ranch ratios were calculated: β 1=0.465, β 2=0.453, β 3=0.079 and β 4=0.004. The results indicate that Nd 3+∶Sr 6YSc(BO 3) 6 c rystal seems to be a potential high-efficient laser material.

关 键 词：OPTICS Nd  3+∶Sr  6YSc(BO  3)  6 crystal crystal growth spectral pa rameters Judd-Ofelt theory rare earths 

分 类 号：O482.3[理学—固体物理]