金红石复相体系浓悬浮体的制备  

Preparing Concentrated Suspension of Rutile Mixture

作　　者：马利国[1] 杨金龙[1] 马天[1] 黄勇[1] 

机构地区：[1]清华大学材料科学与工程系新型陶瓷与精细工艺国家重点实验室,100084

出　　处：《高技术通讯》2003年第10期54-57,共4页Chinese High Technology Letters

基　　金：86 3计划 (2 0 0 1AA3370 6 0 );973规划 (G2 0 0 0 0 6 72 0 3 2 );国家自然科学基金 (5 0 2 32 0 10 )资助项目

摘　　要：胶态成型工艺要求制备高固相含量、低粘度的浓悬浮体。由于复杂的胶体特性 ,金红石典型配方中含有的多种烧结助剂对金红石粉料在水介质中的分散行为往往产生较大影响。本文采用高温煅烧金红石复相体系的方法 ,消除了烧结助剂对制备金红石浓悬浮体的不良影响。通过调节 pH值和分散剂用量 ,优化了金红石粉料在水介质中的分散条件 ,从而成功地制备了体积分数为 5 1 7%的金红石复相体系浓悬浮体。Concentrated suspension with high solid loading and low viscosity is required during colloidal forming processing. Due to complex colloidal character in water medium, many additives included in rutile mixture greatly influenc flow behavior of rutile. In this work, by means of adding a dispersant with a definite dose and adjus ting pH to 10 or so, the mixture is easy to be dispersed by calcining at high temperature and then ball milling, and a concentrated rutile suspension (51.7 vol%) with low viscosity was successfully obtained.

关 键 词：金红石复相体系 胶态成型工艺 浓悬浮体 陶瓷工业 

分 类 号：O648[理学—物理化学]