Adiabatic shear banding of hot-rolling Ti–6Al–4V alloy subjected to dynamic shearing and uniaxial dynamic compression  

作　　者：Yu-Meng Luo Jin-Xu Liu Xing-Wang Cheng Shu-Kui Li Fu-Chi Wang Wen-Wen Guo 

机构地区：[1]China National Key Laboratory of Science and Technology on Materials Under Shock and Impact, School of Materials Science and Engineering, Beijing Institute of Technology

出　　处：《Rare Metals》2015年第9期632-637,共6页稀有金属（英文版）

基　　金：financially supported by the National Natural Science Foundation of China (No.51201013)

摘　　要：Effect of stress state including dynamic shearing and uniaxial dynamic compression on adiabatic shear banding(ASBing) of hot-rolling Ti–6Al–4V(TC4) alloy was investigated. The absorbed energy of specimen before failure was calculated to evaluate the susceptibility to adiabatic shear band(ASB) of TC4 alloy quantitatively.Results show that the susceptibility to ASB of hot-rolling TC4 alloy exhibits obvious anisotropy under both dynamic shearing and uniaxial dynamic compression conditions, but the anisotropy of susceptibility to ASB under dynamic shearing condition exhibits an opposite tendency with that under uniaxial dynamic compression condition. Under the condition of uniaxial dynamic compression, material shows the highest susceptibility to ASB when loaded along transverse direction(TD) of the hot-rolling TC4, while the lowest susceptibility when loaded along rolling direction(RD). However, under the condition of dynamic shearing,the material behaves in the opposite way, demonstrating the lowest susceptibility when loaded along TD of the hotrolling TC4, while the highest susceptibility when loaded along RD.Effect of stress state including dynamic shearing and uniaxial dynamic compression on adiabatic shear banding(ASBing) of hot-rolling Ti–6Al–4V(TC4) alloy was investigated. The absorbed energy of specimen before failure was calculated to evaluate the susceptibility to adiabatic shear band(ASB) of TC4 alloy quantitatively.Results show that the susceptibility to ASB of hot-rolling TC4 alloy exhibits obvious anisotropy under both dynamic shearing and uniaxial dynamic compression conditions, but the anisotropy of susceptibility to ASB under dynamic shearing condition exhibits an opposite tendency with that under uniaxial dynamic compression condition. Under the condition of uniaxial dynamic compression, material shows the highest susceptibility to ASB when loaded along transverse direction(TD) of the hot-rolling TC4, while the lowest susceptibility when loaded along rolling direction(RD). However, under the condition of dynamic shearing,the material behaves in the opposite way, demonstrating the lowest susceptibility when loaded along TD of the hotrolling TC4, while the highest susceptibility when loaded along RD.

关 键 词：Adiabatic shear banding Ti alloy Dynamic compressi 

分 类 号：TG146.23[一般工业技术—材料科学与工程]