T10钢自蔓延高温渗硼共晶化的研究  

Research on Steel T10 Treated by Self-propagating High-temper ature Quick-boriding

作　　者：叶荣昌[1] 葛长路[2] 骆俊 

机构地区：[1]北京科技大学材料科学与工程学院,北京100083 [2]中国矿业大学机电学院,江苏徐州221008 [3]北京南苏新材料科技有限公司,北京100083

出　　处：《金属热处理》2003年第5期30-32,共3页Heat Treatment of Metals

摘　　要：采用自蔓延高温渗硼共晶化技术在T10钢表面获得了具有共晶组织的渗硼层。渗层最大厚度可达1 6mm ,渗层与基体呈冶金结合状态。渗层物相主要由α Fe、Fe3(C ,B)及少量的Fe2 3(C ,B) 6相构成 ,其中 ,Fe3(C ,B)相构成花纹状共晶的骨架 ,α Fe相则分布于其中 ,从而赋予渗层以良好的强度、硬度与韧性。In this paper,a r esearch has been made on steel T10 by th e technology of self-propagating high-te mperature quick-boriding.A eutectic-stru cture borided layer with a maximum thick ness of 1 6 mm is obtained on the sample surface.The borided layer is combined in metallurgy with the matrix.The layer ma inly consists of phases α-Fe,Fe 3(C,B) a nd some Fe 23 (C,B) 6,where Fe 3(C,B) p hase acts as bones of the eutectic struc ture with α-Fe phase among them,which ma kes the layer with good strength,hardnes s and toughness.

关 键 词：自蔓延高温渗硼共晶化 共晶组织 渗硼层 

分 类 号：TG156.8[金属学及工艺—热处理] TG142.41[金属学及工艺—金属学]