Hydrothermal Synthesis and Properties of Open-Framework Mixed-valence Iron Phosphates IIIII21.543FeFe(PO) with Three-dimensional Structure  

作　　者：段丽颖 刘福臣 王恩波 李阳光 胡长文 许林 

机构地区：[1]Institute of Polyoxometalate Chemistry,Department of Chemistry,Northeast Normal University

出　　处：《Chinese Journal of Chemistry》2004年第1期55-59,共5页中国化学（英文版）

基　　金：the National Natural Science Foundation of China (No. 20171010).

摘　　要：The open-framework iron phosphate IIIII21.543FeFe(PO) was hydrothermally synthesized and characterized by elemental analysis, IR, EPR, XPS and single crystal X-ray diffraction analysis. The title compound crystallized in the triclinic, space group P1with a=0.64724(4) nm, b=0.79651(6) nm, c=0.94229(5) nm, =104.447(2)? =108.919(4)? =101.741(4)? V=0.42302(5) nm3, Z=1 and R1 (wR2)=0.0307 (0.0793). Crystal data were collected on a Rigaku R-AXIS RAPID IP diffractometer with Mo K?(=0.071073 nm) at 293(2) K in the range of 2.43埃迹?7.46? The structure of 1 consists of 19 non-hydrogen atoms including three and a half crystallographically in-dependent Fe and three P atoms. Fe(1) connects its symmetrical Fe(1A) through bridging oxygen forming a dimer and the dimers are connected by Fe(4) forming an infinite staircase-like chain. Fe(2) and Fe(3) connect the infinite chains into a layer with bridging oxygen. Layers are interconnected via Fe(4) forming the six-membered and eight-membered channel systems.The open-framework iron phosphate IIIII21.543FeFe(PO) was hydrothermally synthesized and characterized by elemental analysis, IR, EPR, XPS and single crystal X-ray diffraction analysis. The title compound crystallized in the triclinic, space group P1with a=0.64724(4) nm, b=0.79651(6) nm, c=0.94229(5) nm, =104.447(2)? =108.919(4)? =101.741(4)? V=0.42302(5) nm3, Z=1 and R1 (wR2)=0.0307 (0.0793). Crystal data were collected on a Rigaku R-AXIS RAPID IP diffractometer with Mo K?(=0.071073 nm) at 293(2) K in the range of 2.43埃迹?7.46? The structure of 1 consists of 19 non-hydrogen atoms including three and a half crystallographically in-dependent Fe and three P atoms. Fe(1) connects its symmetrical Fe(1A) through bridging oxygen forming a dimer and the dimers are connected by Fe(4) forming an infinite staircase-like chain. Fe(2) and Fe(3) connect the infinite chains into a layer with bridging oxygen. Layers are interconnected via Fe(4) forming the six-membered and eight-membered channel systems.

关 键 词：iron phosphate open framework three-dimensional structure 

分 类 号：O614.8[理学—无机化学]