北方重工50tEBT超高功率电弧炉无富氧泡沫渣工艺  

No-Rich-Oxygen Foam Slag Operating Procedure for a 50 t EBT UHP Arc Furnace at North Heavy Industry Group

作　　者：李登仁 

机构地区：[1]北方重工业集团,包头014033

出　　处：《特殊钢》2004年第1期51-52,共2页Special Steel

摘　　要：北方重工业集团 5 0t偏心炉底出钢超高功率电弧炉冶炼周期为 2h ,采用氧化铁皮作为氧化剂 ,炉料中配入 2 0 %以上生铁 ,控制炉渣碱度 2～ 3 5 ,渣中FeO含量为 15 %～ 2 5 % ,渣量 3 0t。使用泡沫渣埋弧操作后 ,钢液的升温速度由原来的 3 5℃ /min提高到 7 5℃ /min ,4 5钢出钢 [S]为 0 0 12 %～ 0 0 2 0 % ,[P]0 0 0 5 %～ 0 0 0 7% ,电弧炉的炉龄由原来的 5 0炉提高到 15 0炉。With tap to tap time 2 h of steelmaking for a 50 t EBT UHP arc furnace at North Heavy Industry Group, using scale as oxidizing agent, pig iron in charging over 20%, controlling slag basicity 2～3.5, FeO content in slag 15%～25% and total slag amount ～3 t, by using foam slag immersed arc operation the heating speed of liquid steel increased to 7.5 ℃/min from original 3.5 ℃/min, the of 0.45C steel in tapping was 0.012%～0.020%, the was 0.005%～0.007% and the arc furnace life increased to 150 heats from original 50 heats.

关 键 词：超高功率电弧炉 无富氧 泡沫渣工艺 炼钢 