反应烧结制备Ba_2Ti_9O_(20)材料  被引量:4

Preparation of Ba_2Ti_9O_20 Materials via React-sintering Process

在线阅读下载全文

作  者:李蔚[1] 赵梅瑜[1] 吴文骏[1] 

机构地区:[1]中国科学院上海硅酸盐研究所,上海200050

出  处:《无机材料学报》2004年第2期439-443,共5页Journal of Inorganic Materials

摘  要:采用BaCO3和TiO2为原料粉体,经机械球磨后直接成型烧结,可以在1340℃/4h的条件下获得密度达4.49g/cm3的单相Ba2Ti9O20材料.进一步的研究表明,采用高能球磨可以大大降低反应烧结的温度,在1250℃/4h的条件下可获得密度达4.44 g/cm3的单相Ba2Ti9O20材料.高能球磨所获得的粉体颗粒细小、均匀是反应烧结温度低的主要原因.本研究还分析了烧结过程中材料的相组成的变化过程.The preparation of Ba2Ti9O20 materials via react-sintering process was investigated. BaCO3 and TiO2 were used as raw materials, after mechanical milling, the mixed powders were pressed into pellets and sintered directly. The reacting mechanism during sintering process was also investigated. Single phase Ba2Ti9O20 materials with a high density of about 4.49 can be obtained after sintering at 1340degreesC for 4h. More investigations show that the sintering temperature can be obviously lowered by using high-energy milling process instead of common mechanical milling process. Single phase Ba2Ti9O20 materials with a high density of about 4.44 can be obtained under 1250degreesC/4h conditions. Smaller particles and homogeneous distribution of the high-energy milling powders are the main reason for their low sintering temperatures.

关 键 词:钛酸钡 制备 反应烧结 碳酸钡 二氧化钛 高能球磨 相变 微波介质材料 

分 类 号:TM25[一般工业技术—材料科学与工程]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象