包覆型高岭土/二氧化钛纳米复合颗粒的电流变效应  

Electrorheological Effect of Titania-Coated Kaolinite Nanocomposite Particles

作　　者：王宝祥[1] 左朝阳[1] 赵晓鹏[1] 

机构地区：[1]西北工业大学电流变技术研究所,西安710072

出　　处：《无机材料学报》2004年第3期492-496,共5页Journal of Inorganic Materials

基　　金：国家杰出青年科学基金(50025207);863计划(2001AA327130);国家自然科学基金(50272054)

摘　　要：采用溶胶-凝胶法制备了一种新型高岭土/二氧化钛纳米复合电流变液材料.XRD、FT-IR、SEM分析表明TiO_2以纳米晶的形态包覆于高岭土表面.电流变性能测试表明,不同的TiO_2质量比的复合颗粒电流变液效应不同,且都比纯高岭土电流变有显著提高.同时当复合颗粒中TiO_2质量百分比在34％,颗粒硅油体积分数为25％,直流电场为3kV/mm时,高岭土/二氧化钛纳米复合材料电流变液的静屈服应力达3.4kPa,是纯高岭土电流变液的5倍.Kaolinite/TiO2 nanocomposite particles were prepared by sol-gel technique. The analysis of XRD,FT-IR, and SEM shows that the surface of kaolinite is coated by nano-TiO2 crystal. Furthermore the electrorheological effect is associated with the TiO2 mass percent in the nanocomposite particle. When the content of TiO2 in the composite is 34%, E = 3kV/mm, and volume fraction is 25%, the yield stress of kaolinite/TiO2 nanocomposite ERF is 3.4 kPa, which is 5 times of that of kaolinite.

关 键 词：高岭土 二氧化钛 电流变液 溶胶-凝胶法 

分 类 号：TB383[一般工业技术—材料科学与工程] O646[理学—物理化学]