铝阳极氧化膜在NaCl溶液中的电化学性能  

Electrochemical properties of anodized aluminum films in sodium chloride solution

作　　者：赵旭辉[1] 左禹[1] 赵景茂[1] 

机构地区：[1]北京化工大学材料科学与工程学院,北京100029

出　　处：《中国有色金属学报》2004年第4期562-567,共6页The Chinese Journal of Nonferrous Metals

基　　金：国家自然科学基金资助项目(59971005);国家重点基础研究发展规划资助项目(G19990650)

摘　　要：采用交流阻抗法研究了工业纯铝L3阳极氧化膜在中性NaCl溶液中交流阻抗谱的变化规律,比较了未封闭处理与沸水封闭处理后氧化膜的交流阻抗谱的差异,并结合等效电路分析了氧化膜多孔层与阻挡层电化学参数的变化。结果表明,未封闭的阳极氧化膜在NaCl溶液中浸泡初期存在一个自封闭过程,封闭处理明显提高氧化膜多孔层的初始Rp值并降低初始CPEp值;溶液中侵蚀性离子浓度越高,封闭处理提高铝阳极氧化膜的耐蚀性能作用越明显。The electrochemical impedance behaviors of unsealed and sealed anodized aluminum films in sodium chloride solutions were studied by means of electrochemical impedance spectroscopy. The electrochemical parameters for the anodic film were analyzed by an equivalent circuit method. The results reveal that there is an auto-sealing process in sodium chloride solutions for the unsealed anodized aluminum. Boiling water-sealing process obviously increases the initial R_p value of the porous layer and decreases the initial C_(PEp) value. The higher the aggressive ion concentration in the solution, the more effectively the sealing process improves corrosion resistance of the anodized films.

关 键 词：铝 阳极氧化膜 NACL溶液 电化学性能 阳极氧化 交流阻抗 

分 类 号：TG174.451[金属学及工艺—金属表面处理]