影响生长大尺寸和高质量β-BBO晶体的因素  

Influence of Growth Conditions on the Large-sized and High Quality β-BaB_2O_4 Crystal

作　　者：陈伟[1] 江爱栋[1] 王国富[1] 

机构地区：[1]中国科学院福建物质结构研究所

出　　处：《人工晶体学报》2004年第2期227-230,共4页Journal of Synthetic Crystals

摘　　要：本文讨论顶部籽晶法各种生长条件对大尺寸、高质量β BaB2O4晶体的影响,诸如助熔剂、温度梯度、晶体转速、降温速率、籽晶方向等晶体生长工艺参数。采用NaF作为助熔剂、〔001〕向的定向籽晶、接近液面温度梯度为3～8℃/cm、5～20r/min的转速、0.05～0.1℃/h降温速率的生长工艺,使用直径为100mm的铂坩埚,成功地生长出100mm×40mm、光学均匀性为4.326×10 6的大尺寸高质量的β BBO晶体。This paper discussed the influence of growth conditions on the large-sized and high quality β-BaB_2O_4 crystal, such as flux, crystal rotating rate, solution cooling rate, seed orientation and vertical temperature gradient. The high-quality β-BaB_2O_4 crystals with dimensions of 100×40mm^3 and weight of 800g were successfully grown,and the optical homogeneity of as-grown crystal is 4.326×10^(-6).The proper growth condition is as follows:NaF as flux,[001]seed orientation,vertical temperature gradient near solution surface 3-8℃/cm,rotation rate 5-20r/min,cooling rate 0.05-0.1℃/h,Pt crucible with the diameter of 100mm.

关 键 词：β-BBO晶体 低温相偏硼酸钡 非线性光学晶体 晶体生长工艺 助熔剂 降温速率 光学均匀性 

分 类 号：O782.4[理学—晶体学]