ZrO_2层状复合陶瓷压痕开裂力学分析  

Indentation Cracking Mechanical Analysis of ZrO_2 Laminated Ceramics

作　　者：陈蓓[1] 丁培道[2] 程川[3] 

机构地区：[1]重庆大学高电压与电工新技术教育部重点实验室,重庆400030 [2]重庆大学材料科学与工程学院,重庆400030 [3]重庆大学资源与环境工程学院,重庆400030

出　　处：《重庆大学学报（自然科学版）》2004年第7期65-67,71,共4页Journal of Chongqing University

基　　金：国家863计划资助项目(2001AA331050)

摘　　要：在ZrO2层状复合陶瓷中,压痕裂纹的形成除了因塑性区体积变化产生的残余应力外,还与相变应力有关。此外,界面压应力对表面裂纹具有较大的抑制作用。传统的压痕法公式忽略了压痕底下相变应力和界面压应力对压痕开裂和试样断裂的贡献,得到的数据偏小,不能真实反映ZrO2层状复合陶瓷断裂韧性大小。用Indentation-fracture法测ZrO2层状复合陶瓷的断裂韧性更接近真实值。The formation of indentation cracking has some relationship with the transformation stress induced by martensitic transformation, besides the relationship with the residual stress by volume change in the plastic zone in ZrO_2 laminated ceramics. Whereas surface residual compressive stress controls the expansion of surface cracks. Contributions of the transformation driving force and surface compressive stress are not considered in the traditional indentation theory. Therefore, fracture toughness value measured by the traditional method is usually lower than the practical one in ZrO_2 laminated ceramics. When indentation-fracture method is used, the value is more reliable.

关 键 词：ZrO2层状复合陶瓷 压痕法 压痕-断裂法 断裂韧性 

分 类 号：TQ174.75[化学工程—陶瓷工业]