Al5TiB对Mg-8Zn-4Al-0.3Mn镁合金阻尼性能的影响  

Effects of Al5TiB on Damping Properties of Mg-8Zn-4Al-0.3Mn Magnesium Alloys

作　　者：王建强[1] 关绍康[1] 石广新[1] 王迎新[1] 赵红亮[1] 

机构地区：[1]郑州大学材料工程学院,河南郑州450002

出　　处：《热加工工艺》2004年第5期5-7,49,共4页Hot Working Technology

基　　金：河南省高校创新人才工程资助项目(2002-10)

摘　　要：研究了变质剂Al5TiB对Mg-8Zn-4Al-0.3Mn镁合金阻尼性能的影响。结果表明:Al5TiB的加入显著细化了Mg-8Zn-4Al-0.3Mn镁合金晶粒,增大了界面面积,提高了合金的界面阻尼。但是,Al5TiB的加入又促进了Al、Zn原子向基体中的扩散,降低了合金的位错阻尼。加入变质剂Al5TiB后Mg-8Zn-4Al-0.3Mn镁合金的阻尼机制主要是界面阻尼和位错阻尼。二者迭加的结果决定了ZA84镁合金的宏观阻尼行为。The effect of Al5TiB on damping properties of Mg-8Zn-4Al-0.3Mn alloys was studied.The results show that the interface damping capacity of Mg-8Zn-4Al-0.3Mn alloys is improved because of Al5TIB refining the grain of Al5TiB Mg-8Zn-4Al-0.3Mn magnesium alloys; however the dislocation damping capacity is reduced slightly because of Al5TiB promoting the Al、Zn atoms to diffuse to the matrix.The miain damping mechanism of Mg-8Zn-4Al-0.3Mn magnesium alloys with Al5TiB is contribute to the interface damping and the dislocation damping.The addition outcome of two factors determine the macro damping behaviors of ZA84 magnesium alloys.

关 键 词：阻尼 Mg-8Zn-4Al-0.3Mn镁合金 AL5TIB 

分 类 号：TG146.22[一般工业技术—材料科学与工程]