聚醚多元醇分子量对环氧树脂增韧效果的研究  

Study on relation between molecular of polyether polyols and toughening epoxy resins

作　　者：罗炎[1] 何朝霞[1] 陈子方 李长元[1] 

机构地区：[1]桂林电子工业学院信息材料科学与工程系,广西桂林541004 [2]无锡市友联绝缘材料有限公司,江苏无锡214011

出　　处：《绝缘材料》2004年第3期12-16,19,共6页Insulating Materials

基　　金：广西科学基金资助项目 (桂科自0339065)

摘　　要：为了开发新型实用的环氧树脂增韧剂 ,合成了一种新型聚醚多元醇。试验结果表明 ,聚醚多元醇的分子量 (羟值 )对固化体系的初期粘度等性能没有影响 ,对固化体系的力学性能、断裂韧性和热性能等有较大影响。与未改性的环氧树脂相比 ,用FH聚醚多元醇改性环氧树脂的冲击强度增加124 % ,断裂韧性比增加89 % ,断裂能比增加260 %To develop toughening reagent for epoxy resins,a serial of novel polyethers polyols was synthesized.Testing results show that the molecular of polyethers polyols has much affection on mechanic properties,fracture toughness and heat resistance of cured epoxy resins,and less affection on initiate viscosity of modified epoxy resins.In comparison with unmodified epoxy resin,the impart strength of modified epoxy resin by FH type polyether polyols has increased by124%,the fracture toughness ratio by89%,and the fracture energy ratio by260%.

关 键 词：环氧树脂 增韧 断裂韧性 聚醚多元醇 

分 类 号：TM215[一般工业技术—材料科学与工程] TQ323.5[电气工程—电工理论与新技术]