杨木NS-AQ法高得率化学浆氧脱木素的研究  

Oxygen Delignification of Aspen NS-AQ High-Yield Chemical Pulp

作　　者：张运展[1] 唐凤华[1] 孙文胜[2] 鲁国栋[2] 

机构地区：[1]大连轻工业学院,辽宁大连116034 [2]石岘造纸厂,吉林图们133101

出　　处：《中国造纸学报》2004年第1期11-14,共4页Transactions of China Pulp and Paper

摘　　要：对NS-AQ法杨木高得率化学浆(粗浆得率63.70％,细浆得率59.23％)的氧脱本素进行了研究。结果表明,在实验室条件下,适宜的氧脱木素条件是:浆浓11％,氧气压力 0.6MPa,温度85℃,时间80min,用碱量5％,硫酸镁用量0.3％。适宜条件下的氧脱木素结果是:卡伯值约下降3/4(由37.3降至9.1),粘度约下降1/3(由1340mL/g降至873mL/g),白度提高14.9(由50％ISO提高至64.9％ISO)个百分点,返黄值大幅度(由4.53降至0.90)下降,浆的损失率为6.7％(得率为93.3％),总得率为55.26％。Oxygen delignification of Aspen NS-AQ high-yield chemical pulp (unscreened yield 63.70%, screened yield 59.23%) was stud- ied. The results indicated that the suitable conditions of oxygen delignification at laboratory are: the consistency of pulp 11%, oxygen pressure 0.6 MPa, temperature 85 ℃, reaction time 80 min, the charge of NaOH 5%, and MgSO_4 0.3%. As a consequence of oxygen delignification, the kappa number of the pulp decreases from 37.3 to 9.1, intrinsic viscosity decreases hom 1340 to 873 mL/g, brightness increases from 50 to 64.9%ISO, yellowing value decreases from 4.53 to 0.90, the loss of pulp 6.7% and total yield (on chip) 55.26%.

关 键 词：杨木 NS-AQ法 高得率化学浆 氧脱木素 造纸 制浆 TCF可漂性 

分 类 号：TS721.1[轻工技术与工程—制浆造纸工程] TS74