Fe79Zr8W1B12合金的微观结构及热性能研究  

Microstructure and Thermal Property of Fe79Zr8W1B12 Alloy

作　　者：杨玉蓉[1] 刘立[1] 闫国民[1] 皮艳梅[1] 

机构地区：[1]黑河学院物理化学系,黑龙江黑河

出　　处：《物理化学进展》2015年第2期19-23,共5页Journal of Advances in Physical Chemistry

基　　金：黑龙江省教育厅科学技术研究资助项目(12541572);黑河学院青年科研拔尖人才支持计划资助(2014)。

摘　　要：采用熔体快淬法制备Fe79Zr8W1B12合金非晶薄带,在不同退火温度下对其进行热处理。结合差热分析仪(DTA),X射线衍射仪(XRD)和透射电镜(TEM)等测试技术对Fe79Zr8W1B12合金的热性能和微观结构进行研究。结果表明:Fe79Zr8W1B12合金的晶化过程为非晶→剩余非晶 + α-Fe + α-Mn型→α-Fe + Fe3Zr + ZrFe2 + BFe。由于α-Fe和α-Mn型相具有不同的形核速率导致激活能被划分为两个区间。Fe79Zr8W1B12 amorphous alloy was prepared by melt-spinning and annealed at different temper-atures. The thermal property and microstructures were investigated by differential thermal anal-ysis (DTA), X-ray diffraction (XRD) and transmission electron microscope (TEM). The crystallization progress of Fe79Zr8W1B12 alloy is as follows: amorphous → residual amorphous + α-Fe + α-Mn type → α-Fe + Fe3Zr + ZrFe2 + BFe. The activation is divided into two intervals because the α-Fe and α-Mn type phases have different nucleation rates.

关 键 词：非晶 微观结构 热性能 

分 类 号：TB3[一般工业技术—材料科学与工程]