工艺参数对5754铝合金组织和性能的影响  

Effect of Process Parameters on Microstructure and Properties of 5754 Aluminum Alloy

作　　者：陈纪强 戴青松 桑高锋[1] 赵明伟 

机构地区：[1]广西柳州银海铝业股份有限公司,广西柳州 [2]中南大学材料科学与工程学院,湖南长沙

出　　处：《材料科学》2018年第3期137-143,共7页Material Sciences

基　　金：广西创新驱动重大专项(桂科AA17202011);广西科技计划项目(桂科AA16380039)。

摘　　要：以5754铝合金为研究对象,研究了变形量、退火温度、退火时间等因素对5754合金板材组织和性能的影响。结果表明,5754合金板材加工硬化现象显著,随着变形量的增加,其抗拉强度和屈服强度不断增大,而延伸率则逐渐降低,且5754合金板材退火时间对力学性能的影响小于退火温度。Taking the 5754 aluminum alloy for automobile as the research object, the effect of cold rolling deformation, heat holding time and heat holding temperature on the properties and microstructure of alloy were studied. The results show that the work hardening of 5754 alloy sheet is significant. With the increasing of cold rolling deformation, the tensile strength and yield strength of alloy plates increase gradually, while the elongation decreases. And the annealing time on the me-chanical propertied of 5754 aluminum alloy is less sensitive than the annealing temperature.

关 键 词：5754铝合金 冷变形 退火工艺 组织性能 

分 类 号：TG14[一般工业技术—材料科学与工程]