Importance of Dynamic Mechanical Analysis to Predict Performance of the Polyvinyl Acetate Wood Adhesives in Summer Season  

作　　者：Ravindra V. Gadhave Ravindra V. Gadhave(Department of Polymer and Surface Engineering, Institute of Chemical Technology, Mumbai, India)

机构地区：[1]Department of Polymer and Surface Engineering, Institute of Chemical Technology, Mumbai, India

出　　处：《Open Journal of Polymer Chemistry》2022年第3期93-100,共8页高分子化学期刊（英文）

摘　　要：Conventionally available Polyvinyl acetate (PVAc) wood glues are polyvinyl alcohol (PVA) stabilized, with drawbacks like poor strength at high humidity, poor strength at high temperature and workability at low-temperature. PVAc is non-resistant to high humidity, and if such adhesive bonds are exploited in a highly humid environment, its strength substantially decreases. Sufficiently water-resistant adhesive bonds are achieved by modifying PVAc dispersion with special chemicals like acrylic acid (AA) and N-methylol acrylamide (NMA) as a co-monomer, Silanes, and ethylene modified PVA. The Lewis acids like aluminium chloride and aluminium nitrate are used as cross-linkers. So PVAc adhesives are classified as reactive and non-reactive glue. Application of non-reactive D1 (as per EN 204-205) and reactive D2 and D3 (as per EN 204-205) adhesives for bonding laminate on plywood is a regular practice in the Indian market. In summer time, Crack formation was seen in laminate bonded with reactive D2 and D3 adhesives in regions where the room temperature was above 45°C. However, if the same laminate substrates were bonded with non-reactive D1, no cracks were seen. To analyse the above phenomenon, we have done Dynamic mechanical analysis of non-reactive D1, reactive D2 and D3 adhesive.Conventionally available Polyvinyl acetate (PVAc) wood glues are polyvinyl alcohol (PVA) stabilized, with drawbacks like poor strength at high humidity, poor strength at high temperature and workability at low-temperature. PVAc is non-resistant to high humidity, and if such adhesive bonds are exploited in a highly humid environment, its strength substantially decreases. Sufficiently water-resistant adhesive bonds are achieved by modifying PVAc dispersion with special chemicals like acrylic acid (AA) and N-methylol acrylamide (NMA) as a co-monomer, Silanes, and ethylene modified PVA. The Lewis acids like aluminium chloride and aluminium nitrate are used as cross-linkers. So PVAc adhesives are classified as reactive and non-reactive glue. Application of non-reactive D1 (as per EN 204-205) and reactive D2 and D3 (as per EN 204-205) adhesives for bonding laminate on plywood is a regular practice in the Indian market. In summer time, Crack formation was seen in laminate bonded with reactive D2 and D3 adhesives in regions where the room temperature was above 45°C. However, if the same laminate substrates were bonded with non-reactive D1, no cracks were seen. To analyse the above phenomenon, we have done Dynamic mechanical analysis of non-reactive D1, reactive D2 and D3 adhesive.

关 键 词：Polyvinyl Acetate Wood ADHESIVE CRACKING Dynamic Mechanical Analysis 

分 类 号：TQ433[化学工程]