Zr取代TiMn合金中的部分Ti对合金储氢性能的影响  

INFLUENCE OF PARTIAL SUBSTITUTION OF Zr FOR Ti ON HYDROGEN STORAGE PERFORMANCE OF TiMn BASED ALLOYS

作　　者：吴铸[1] 李志林[1] 倪君[1] 黄铁生[1] 黄太仲[1] 徐乃欣[1] 

机构地区：[1]中国科学院上海微系统与信息技术研究所,上海200050

出　　处：《化工学报》2004年第S1期172-175,共4页CIESC Journal

基　　金：国家高技术研究发展计划资助项目(No.2003AA515022)

摘　　要：讨论了Zr取代TiMn合金中的部分Ti对其吸放氢性能的影响。XRD分析结果表明:合金的晶胞体积随合金中zr含量的增加而增大。PCT测试表明合金的最大吸氢量随合金中Zr含量的增加而增大,吸氢平台压力随合金中Zr含量的增加而降低;合金Ti_(0.9)Zr_(0.1)Mn_(1.4)具有最大的可逆吸氢量。由于Zr元素的引入,合金吸放氢过程的焓变和熵变均有所增加。Influence of partial substitution of Zr for Ti on hydrogen storage performance of TiMn based alloys was discussed. XRD results showed that the crystal cell volume was enlarged by substitution of Zr for Ti. PCT tests showed that the maximum hydrogen absorption content increased with increasing Zr content. Thus the hydrogen absorbing plateau pressure decreased simultaneously. Ti_(0.9) Zr_(0.1)Mn_(1.4) alloy has the highest reversible hydrogen storage capacity among all the alloys. Enthalpy and entropy changes...

关 键 词：TiMn储氢合金 PCT XRD 焓变 