ZnO纳米线的催化合成及其光致发光性能  

Catalytic Synthesis and Photoluminescence property of ZnO nanowires

作　　者：于伟东[1] 李效民[1] 高相东[1] 边继明[1] 陈同来[1] 

机构地区：[1]高性能陶瓷和超微结构国家重点实验室 中国科学院上海硅酸盐研究所 上海

出　　处：《纳米科技》2004年第1期-,共4页

摘　　要：采用气相传输法,以金膜为催化剂,氧化锌和石墨混合粉末为锌源,制备氧化锌纳米材料。研究获得氧化锌纳米线的光致发光性能。初步探索了氧化锌纳米线的生长机理。实验结果表明,当衬底温度为600℃时,金颗粒的催化性能得到了较好的发挥,形成长度大于10μm,直径小于80 nm的均匀致密的氧化锌纳米线膜。这种氧化锌纳米线具有紫外发光特性。低于600℃时,锌氧蒸汽发生了自凝结,进而在金颗粒间隙形成氧化锌带(400℃时),或在金颗粒上吸附聚集形成花状氧化锌纳米棒(200℃时)。而在高于600℃时,金颗粒析出的锌迅速挥发或氧化、长大,出现了稀疏的针状氧化锌和颗粒。氧化锌纳米线可能的生长模式为"底端生长"模式。Abstract ZnO nanomaterial was synthesized by the vapor transport method with the Zn source by the pyrolysis of ZnO with graphite powder and the catalyst of Au film. The results show that the dense and uniform ZnO nanowires with the length of around10μm and the diameter of about 80nm were acquired under the substrate temperature of 600℃. The UV-light with the wavelength of 380 nm was detected from this kind of nanowires. When the temperature decreases to 400℃ and 200℃, the ZnO nanobelts and nanoflowers were ...

关 键 词：ZnO 纳米线 衬底温度 光致发光 生长机理 

分 类 号：TB381[一般工业技术—材料科学与工程]