磨料对陶瓷摩擦材料摩擦性能的影响  

Effects of Abrasives on Friction Performance of Ceramic Friction Materials

作　　者：焦龙[1] 吕亚非[1] 

机构地区：[1]北京化工大学新型高分子材料的制备与加工北京市重点实验室,北京100029

出　　处：《润滑与密封》2008年第8期9-11,50,共4页Lubrication Engineering

基　　金：国家自然科学基金项目(50673012);帝人特威隆(德国)研究基金项目

摘　　要：研究了3种不同硬度的磨料(碳化硅、氧化铝、硅酸锆)及其含量对陶瓷摩擦材料摩擦性能的影响。磨料在摩擦材料中的主要作用是改变摩擦和磨损机制,从无磨料时的粘合摩擦磨损机制转变为磨料存在的磨粒摩擦磨损机制。磨料的硬度越大,磨粒摩擦效应越大,提高摩擦因数的效果越好,但磨损率也越大,对摩擦盘的破坏也越严重。实验结果表明,磨料含量对摩擦因数的影响存在一个临界值,约为0.056(体积分数)。磨料含量低于临界值,对摩擦因数的提高作用非常明显,而高于临界值,对提高摩擦因数的作用减弱。The effects of three abrasives,silicon carbide(SiC),alumina(Al2O3),zircon(ZrSiO4)on friction performance of ceramics brake friction materials were studied.The friction materials without abrasives exhibit lower friction coefficient and good specific wear rate.Addition of abrasives to the friction materials,friction coefficient increases and the specific wear rate depresses.Abrasives damage the cast iron disc.The role of the abrasives is to change the friction and wear mechanisms from adhesion to abrasion.The...

关 键 词：陶瓷摩擦材料 摩擦性能 磨料 碳化硅 氧化铝 硅酸锆 

分 类 号：TB302.3[一般工业技术—材料科学与工程]